Among high-speed steel and die steel plates, thin plates are the main products, which are used to manufacture cutting tools such as circular saw blades, paper splitting knives, flat circular knives, and cold shearing knives, which are widely used in metal/paper/plastic/food processing industries and Machinery manufacturing industry.
In the production process of Zhejiang Zhongjian sheet, the cross-rolling process is adopted to give full play to the advantages of large deformation rate. The subsequent vacuum annealing in a protective atmosphere avoids decarburization and restores the superplasticity of the steel. Finally, cold rolling is performed to obtain carbides with uniform distribution and fine particles, and the thickness tolerance, shape and surface quality of the sheet are controlled at the best.
|
通用鋼種 Typical steel grades |
高速鋼
High Speed Steel
|
鋼種 Brand Name |
國標(biāo) GB Type |
歐標(biāo) Mat.-No. |
美標(biāo) AISI/BS type
|
日標(biāo) JIS type |
通用化學(xué)成分% Typical Analysis % |
退火態(tài)硬度HB Annealed/hardness |
淬火硬度°C Hardness in HRC after quenching °C |
||||||||
|
數(shù)據(jù)表 Data Sheet |
(Ident.No.) |
C |
Si |
Mn |
Cr |
Mo |
V |
W |
Co |
Ni |
HB max. |
HRC |
|||
|
M2 |
0.86-0.91 |
0.30-0.40 |
0.20-0.40 |
3.80-4.20 |
4.80-5.20 |
1.80-2.10 | 5.80-6.20 |
/ |
/ |
≤250 |
63-65 |
||||
| W6 | 0.86-0.91 | 0.3-0.4 | 0.2-0.4 | 3.8-4.0 | 4.5*4.7 | 1.70-1.90 | 5.50-6.00 | / | / | ≤250 | 63-65 | ||||
|
W5 |
0.92-0.96 |
0.81-1.20 |
0.20-0.40 |
3.80-4.00 |
1.40-1.70 |
0.90-1.20 | 4.60-4.90 |
/ |
/ |
≤250 |
63-65 |
||||
|
M42 |
0.91-0.95 |
0.30-0.40 |
0.20-0.40 |
3.80-4.20 |
4.80-5.20 |
1.80-2.10 | 5.80-6.20 |
1.80-2.20 |
/ |
≤250 |
64-66 |
||||
|
DF9 |
0.92-0.96 |
0.80-1.20 |
0.20-0.40 |
3.80-4.00 |
2.70-3.20 | 1.20-1.60 | 4.60-4.90 |
1.80-2.0 |
/ |
≤250 |
63-64 |
||||
|
W18 |
0.78-0.85 |
0.30-0.40 |
0.30-0.40 |
3.80-4.20 |
/ |
1.00-1.40 |
17.50 18.20 |
/ |
/ |
≤250 |
63-64 |
||||
|
M35 |
0.90-0.98 |
0.30-0.40 |
0.30-0.40 |
3.80-4.20 |
4.80-5.20 |
1.80-2.10 |
5.80-6.20 |
4.50-5.20 |
/ |
≤250 |
64-66 |
||||
|
W16 |
0.78-0.85 |
0.30-0.40 |
0.30-0.40 |
3.60-4.20 |
/ |
0.65-1.00 |
14.5-15.2 |
/ |
/ |
≤250 |
63-64 |
||||
|
M5 |
0.80-0.85 |
0.50-0.70 |
0.30-0.40 |
3.90-4.10 |
2.30-2.70 |
1.20-1.50 |
5.40-6.00 |
/ |
/ |
≤250 |
63-64 |
||||
|
W4 |
0.88-0.98 |
0.50-1.00 |
0.20-0.40 |
3.50-4.20 |
2.50-3.50 |
1.00-1.20 |
3.50-4.30 |
/ |
/ |
≤250 |
63-64 |
||||
冷作模具鋼
Cold Work Steel
|
鋼種 Brand Name |
國標(biāo) GB Type |
歐標(biāo) Mat.-No. |
美標(biāo) AISI/BS type
|
日標(biāo) JIS type |
通用化學(xué)成分% Typical Analysis % |
退火態(tài)硬度HB Annealed/hardness |
淬火硬度°C Hardness in HRC after quenching °C |
||||||||
|
數(shù)據(jù)表 Data Sheet |
(Ident.No.) |
C |
Si |
Mn |
Cr |
Mo |
V |
W |
Co |
Ni |
HB max. |
HRC |
|||
|
Cr12MoV |
1.45-1.70 |
≤0.40 |
≤0.40 |
11.0-12.5 |
0.40-0.60 |
0.15-0.30 | / |
/ |
/ |
≤230 |
58-60 |
||||
| D2 | 1.40-1.60 | 0.30-0.60 | 0.30-0.60 | 11.50-12.50 | 0.80-1.00 | 0.55-0.70 | / | / | / | ≤230 | 58-60 | ||||
|
1.2379 |
1.50-1.60 |
0.10-0.40 |
0.15-0.45 |
11.0-12.0 |
0.80-0.85 |
0.80-0.85 | / |
/ |
/ |
≤230 |
58-60 |
||||
|
DC53 |
0.95-1.05 |
0.90-1.10 |
0.35-0.45 |
8.0-8.75 |
2.0-2.50 |
0.40-0.60 | / |
/ |
/ |
≤230 |
58-60 |
||||
|
Cr8V2 |
1.10-1.20 |
0.80-1.20 |
0.30-0.50 |
8.0-9.0 |
1.40-1.60 | 1.90-2.10 | 1.40-1.60 |
/ |
/ |
≤230 |
58-60 |
||||
|
1.2360 |
0.48-0.55 |
0.80-1.05 |
0.30-0.50 |
7.60-8.40 |
1.25-1.60 |
0.35-0.50 |
/ |
/ |
/ |
≤230 |
58-60 |
||||
|
1.2080 |
1.90-2.20 |
0.10-0.40 |
1.15-0.45 |
11.0-12.0 |
/ |
/ |
/ |
/ |
/ |
≤230 |
58-60 |
||||
|
L5 |
0.98-1.05 |
0.25-0.38 |
0.50-0.70 |
5.20-5.50 |
1.05-1.15 |
0.20-0.30 |
≤0.30 |
/ |
/ |
≤230 |
58-60 |
||||
|
D3 |
2.00-2.20 |
0.10-0.60 |
0.20-0.60 |
11.5-13.00 |
/ |
/ |
/ |
/ |
/ |
≤230 |
58-60 |
||||
|
D4 |
2.05-2.40 |
0.10-0.60 |
0.10-0.60 |
11.0-13.0 |
0.70-1.20 |
0.15-1.00 |
/ |
/ |
/ |
≤230 |
58-60 |
||||
|
D2D |
1.40-1.60 |
0.30-0.60 |
0.30-0.60 |
11.50-12.50 |
0.90-1.20 |
0.80-1.00 |
/ |
/ |
/ |
≤230 |
58-60 |
||||
| 211 | 0.98-1.05 | 0.80-1.00 | 0.20-0.40 | 4.30-4.50 | 0.50-0.70 | 0.30-0.40 | 1.30-1.50 | / | / | ≤230 | 58-60 | ||||
|
尺寸公差 SIZE TOLERANCES |
板材類（十字軋制、保護氣氛退火態(tài)、表面處理、可定尺/不定尺）
Sheets (cross rolled, descaled, annealed in protective atmosphere, flattened, sheared or saw cut)
經(jīng)供需雙方協(xié)議，可供應(yīng)其他尺寸鋼板或其他軋制精度的鋼板
|
厚度 Nomin.Thickness |
厚度公差 Thickness tolerance |
不平度 min. mach. allow per side |
通用寬度-長度 typical dimensions |
不定尺 random size |
定尺 specified size |
|||
| mm | mm | mm | mm | mm | mm | mm | mm | mm |
|
寬度 Width |
長度 Length |
寬度 Width |
長度 Length |
寬度 Width |
長度 Length |
|||
| ≥ 0.60 < 1.50 | - 0 / + 0.10 | 0,15 | ≥ 500 < 800 | 1500-3000 |
按供需方協(xié)議執(zhí)行 |
按供需方協(xié)議執(zhí)行 |
-0/+5 | -0/+10 |
| ≥ 1.50 < 2.40 | - 0 / + 0.20 | 0,15 | ≥ 600 < 1000 | 1500-3000 | ||||
| ≥ 2.50 < 4.00 | - 0 / + 0.30 | 0,15 | ≥ 600 < 1000 | 1500-3000 | ||||
| ≥ 4.00 < 7.00 | - 0 / + 0.40 | 0,15 | ≥ 600 < 1000 | 1000-2000 | ||||
| ≥ 7.00 < 10.00 | - 0 / + 0.50 | 0,15 | ≥ 500 < 800 | 1000-2000 | ||||
| ≥ 10.00-12.00 | - 0 / + 0.60 | 0,20 | ≥ 500 < 800 | 1000-2000 | ||||
圓鋸片類（激光切割，中心孔/定位孔按供需協(xié)議定制）
Discs (laser cut, with centre hole and pin holes on request)
| 直徑/ diameter | 201- < 302mm | 302- < 352mm | 352- < 452mm | ||||||
|
厚度 / thickness mm |
1.5 < 2.8 | 2.8 - < 3.3 | 3.3- <= 4.3 | 1.9 < 2.8 | 2.8- < 3.3 | 3.3- <=4.3 | 2.3- < 2.8 | 2.8 - < 3.3 | 3.3 - <=5.5 |
| 公差 / tolerances | |||||||||
|
厚度公差 / OD mm |
+0.15/ -0 | +0.20/-0 | +0.20/-0 | +0.15/ -0 | +0.20/-0 | +0.20/-0 | +0.15/ -0 | +0.20/-0 | +0.20/-0 |
|
中心孔 / centre hole mm |
+0/-0,20 | +0/-0,20 | +0/-0,20 | +0/-0,20 | +0/-0,20 | +0/-0,20 | +0/-0,20 | +0/-0,20 | +0.20/-0 |
|
定位孔 / pin hole mm |
+ / - 0,1 | + / - 0,1 | + / - 0,1 | + / - 0,1 | + / - 0,1 | + / - 0,1+ / - 0,1 | + / - 0,1 | + / - 0,1 | + / - 0,1 |
|
激光切割成型 Laser Cut Shape |
|
形狀與圖紙文件上的尺寸、公差要求一致 Lasercut shapes as per drawing or DXF-file/ tolerances to be agreed |
|
脫碳 Decarburisation |
||
|
板材厚度 Sheet thickness |
高速鋼 High Speed Steel |
模具鋼 Cold Work Steel |
|
0.15-3.50 |
max. 3 % 厚度 | max. 3 % 厚度 |
| 4.00-6.00 mm | max. 3 % 厚度 | max. 3 % 厚度 |
| 6.00-7.00mm | max. 3 % 厚度 | max. 3 % 厚度 |
| 7.00-12.00mm | ≤0.30mm | ≤0.30mm |